A View in the Future of the Melting Technology and Refractory Materials for the Glass Industry
Revision
Volume 2, Issue 2, Pages 69-74
Abstract
The present article describes a cost-effective alternative to traditional methods for refining refractory bricks in contact with glass melt and two glass melting technologies, which could be applied as future technology in the glass industry. The refractory bricks were treated by integrating aluminium as a reducing agent into the ceramic structure of the bricks. With this technology it is possible to increase the interfacial tension, thus counteracting the infiltration of pores with melt as well as the progress of corrosion. The melting technologies are the submerge combustion melter and the segmented thin film melter. The submerge combustion melter is a technology suitable for melting the batch very fast and has a specific melting rate of about 20 t/(m² . d). The segmented thin film melter has the advantage of lower fining temperature and a similar melting rate like the standard technology.
Keywords
Submerge combustion melter, rnsegmented thin film melter, glass melt, corrosion of refractories, infiltrating and refining of rnrefractoriesrnrn
References
[1] Jebsen-Marwedel, H.; Brückner, R.: Glastechnische Fabrikationsfehler. Springer Verlag, 3. Aufl. 1980
[2] Jebsen-Marwedel, H.: Blasenbildung in Glasschmelzen aus Poren feuerfester Steine. Glastechn. Ber. 20 (1942) 221–227
[3] Tiegs, T.N.; Montgomery, F.C.; Blue, C.A.: High-density infrared surface treatments of refractories. U.S. Department of Energy, Office of Energy Efficiency & Renewable Energy, 2005, pp. 1–45
[4] Hessenkemper, H.; Weigand, R.: Increasing the service life of glass melt contact refractories. Refractories Manual (2009) 47–49
[5] Submerged Combustion Melting. July 2004. This article is taken from the website of the GTI-GaTechnology Institute: http://www.glas-technology.org/webroot/app/xn/xd.aspx?it=enweb&xd=4reportspubs4_8focussubmerged- combustionmelting.xml
[6] Ross, C.P.; Tincher Gabe, L.: Glass melting technology: a technical and economical assesment. Glass Manufacturing Industrial Council and US Department of Energy Office of Industrial Technologies, contract #DE-FC36-02D14315, August 2004, Submerge Combustion Melting, pp. 150–159
[7] Henry, G.; Brichard, E.: Verfahren und Ofen zum Schmelzen von Glas und dgl., Patent DE000000729098A, February 1939
[8] Glaverbel: Schachtofen zum Schmelzen und Verarbeiten von verglasbaren Produkten, wie Glas, Email od. dgl., und Verfahren zum Herstellen und Aufrechterhalten einer aus erstarrtem Material der Schmelze bestehenden Schicht an den Innenseiten der Schmelzwanne des Schachtofens. Patent AT000000243451B, November 1965
[9] Pieper, H.: Verfahren und Vorrichtung zum Schmelzen von Glas mit Wärmerückgewinnung. Patent DE000010029983C2, June 2006
[10] Hessenkemper, H., Technical University of Mining and Technology Freiberg, Professorship of Glass and Enamel Technology, Heiko. This email address is being protected from spambots. You need JavaScript enabled to view it.
[11] Schelinski, S.: Das Schnellschmelzverfahren, eine branchenübergreifende, robuste und flexible Lösung. Neueste Nachrichten Nr.14, 22.04.2009. The artical can be found at http://www.glasmuseum-weisswasser.de /nn.htm
[12] Berg, S.: Untersuchungen zum Schalleinsatz im Glasschmelzprozess. Diss. at the Technical University of Mining and Technology Freiberg, 2009
[13] Saint-Gobain: Verfahren und Einrichtung zur Läuterung des Flüssigen in dem Läuterraum eines Glasschmelzofens. Patent DE000000476744A, Mai 1929
[14] Gosudarstvennyi nauchno-issledovatelskij institut stekla, Moskwa: Anlage zum Schmelzen von Glas, Patent DE000001771299B, Mai 1968
[15] Pieper, H.: Verfahren und Glasschmelzofen zum Herstellen von hochschmelzenden Gläsern mit verdampfbaren Komponenten Patent DE000019710351C1, March 1993
[16] Nebel, R.: Die Läuterbank als konstruktives Element des Glasschmelzofenbaus. 74. Deutsche Glastechn. Tagung, Ulm 1966. HVG-Information Nr. 1966
[17] K.A. Pchelyakov et al.: Bubbling and fining molten glass in continuous tank furnaces. UDC 666.1.031.2:661.1.031.15. Translated from Steklo i Keramika No. 1 (1973) 13–16
[18] Wiltzsch, S.: Segmented-Dünnschichtschmelzer: ein neues Schmelzkonzept und Fragestell- ungen zur konstruktiven Auslegung. Advanced training course „Neuentwicklungen in der Glasindustrie“, Freiberg, 30.9–02.10.2009
[19] Fleischmann, B.: Refraktärwerkstoffe für den Bau von Glasschmelzöfen. HVG-Advanced training course „Glasschmelzofenbau”, 2005
Copyright
© 2010 Göller Verlag