Equilibrium Phase Relations in the Al2O3–CaO–Cr2O3 System in Air
Centre for Pyrometallurgy, Department of Materials Science & Metallurgical Engineering, University of Pretoria, Pretoria/South Africa
Volume 8, Issue 1, Pages 70 - 74
Cr2O3 can be present in refractory monolithic castables either as a specific addition or as a residual element present in certain raw materials. The transformation of Cr(III) to Cr(VI) during the use of refractory monolithics can cause subsequent problems with disposal of the used refractory lining. It is therefore important to study the degree of Cr(VI) formation as well as its formation mechanism from a fundamental perspective. This study investigated a simplified system of Al2O2 and CaO in the presence of Cr2O3, representative of a system commonly found in refractory castables. Equilibrium phase relations in the Al2O3–CaO–Cr2O3 system in air were investigated in this study. Samples were prepared by varying the Al2O3 contents in the range of 50–80 mass-%. Cr2O3 concentrations up to 4 mass-% and equilibrium temperatures up to 1573 K were used. After equilibrium was reached, the samples were quenched in liquid nitrogen. The phases in the quenched samples were studied using XRD analysis. The results indicated that a Cr(VI)-containing phase Ca4Al6CrO16 with a hauyne crystal structure forms in this system. The water soluble Cr(VI) in the quenched samples was quantified using the diphenylcarbazide spectrophotometric method according to the TRGS 613 standard. The water soluble Cr(VI) in all samples exceeded the allowable European limit.
Al2O3–CaO–Cr2O3, phase relations, calcium alumina cement, Cr(VI), Ca4Al6CrO16
 Sanchez-Ramos, S.; et al.: Analytical and mineralogical studies of ore and impurities from a chromite mineral using X-ray analysis, electrochemical and microscopy techniques. Talanta 74 (2008)  1592–1597  Richard, F.C.; Bourg, A.C.M.: Aqueous geochemistry of chromium – a review. Water Res. 25 (1991)  807–816  Dayan, A.D.; Paine, A.J.: Mechanisms of chromium toxicity, carcinogenicity and allergenicity: Rev. of the literature from 1985 to 2000. Hum. Exp. Toxicol. 20 (2001)  439–451  Frias, M.; de Rojas, M.I.S.: Total and soluble chromium, nickel and cobalt content in the main materials used in the manufacturing of Spanish commercial cements. Cem. Concr. Res. 32 (2002)  435–440  Tandon, R.; Aarts, B.: Chromium, nickel and cobalt contents of some Australian cements. Contact Dermatitis 28 (1993)  201– 205  Wahlberg, J.E.; Lindstedt, G.; Einarsson, O.: Chromium, cobalt and nickel in Swedish cement, detergents, mold and cutting oils. Berufs- Dermatosen 25 (1977)  220–228  Frias, M.; et al.: Contribution of toxic elements – hexavalent chromium in materials used in the manufacture of cement. Cem. Concr. Res. 24 (1994)  533–541  Frias, M; Rojas, M.I.S.: Determination and quantification of total chromium and water-soluble chromium contents in commercial cements. Cem. Concr. Res. 25 (1995)  433–439  Stephan, D.; et al.: High intakes of Cr, Ni, and Zn in clinker Part I. Influence on burning process and formation of phases. Cem. Concr. Res. 29 (1999)  1949–1957  Sinyoung, S.; et al.: Chromium behavior during cement-production processes: A clinkerization, hydration, and leaching study. J. Hazard. Mater. 191 (2011) [1–3] 296–305  TRGS 613: The Technical Rules for Hazardous Substance, 2002  N.N.: Slag Atlas. 2nd ed., Düsseldorf 1995  Antao, S.M.; Hassan, I.; Parise, J.B.: Chromate aluminate sodalite, Ca8Al12O24(CrO4)2: Phase transitions and high-temperature structural evolution of the cubic phase. Can. Mineral. 42 (2004) 1047–1056  EU directive 2003/53/EC: Restrictions on the marketing and use of cements and cementcontaining preparations, 2003  Taylor, H.F.W.: Cement Chemistry. 2nd ed., London 1997  He, H.Y.; Suito, H.: Immobilization of hexavalent chromium in aqueous solution through the formation of 3CaO·(Al,Fe)2O3·Ca(OH)2· xH2O phase, ettringite and C–S–H gel. ISIJ Int. 42 (2002)  139–145
Göller Verlag GmbH