Comparison of Cement- and Hydratable Alumina-Bonded Alumina-Spinel Materials for Steel Ladle Purging Plugs

Andreas Buhr1, Harald Harmuth2, Bin Long3, Jerry Dutton4, In-Ho Jung5, Shengli Jin6

1 Almatis GmbH,Frankfurt/Germany
2 Chair of Ceramics, Montanuniversitaet Leoben/Austria
3 Almatis Qingdao/China
4 Stourbridge/Great Britain
5 McGill University Canada/Canada
6 Chair of Ceramics, Montanuniversitaet Leoben/Austria

Revision 29.04.2017, 09.05.2017

Volume 9, Issue 3, Pages 93 - 106

Abstract

This paper provides a summary of extended investigations performed on cement- and hydratable alumina bonded refractory materials for steel ladle purging plugs. The main wear factors of purging plugs are erosion due to intense stirring, corrosion by iron-oxide slag during oxygen lancing, and spalling due to thermal cycling. These were addressed in the investigation by theoretical thermodynamic evaluations using FactSage, mechanical property testing including hot modulus of rupture, and fracture behaviour testing using the wedge-splitting test. In addition, microstructural investigations were performed in order to explain differences in the material. The results provide a basis for assessment of different binder concepts especially for the purging plug application. These indicate the potential which hydratable alumina bonded materials could have in this area. Industrial and academic partners of the FIRE-network from three different continents have successfully cooperated in this study.

Keywords

Al2O3–MgO–CaO, FactSage analysis, cement bonded castable, no-cement castable, hydratable alumina, fracture behaviour, spalling, microstructure, steel ladle purging plug

References

[1] Chaudhuri, S.; Stein, D.: Application of new gas purging systems in ladle metallurgy. Interceram (1992) 313–316 [2] Becker, J.U.; et al.: Purging plugs for steel ladles-laboratory and plant results from a BOF steel plant. UNITECR 1997, New Orleans, USA, 143–152 [3] Hiroaki, E.; et al.: Development of long-life slit plug material for steel ladle. UNITECR 1999, Berlin, Germany, 308–311 [4] Zhao, M.: Stirring units for LF/VD ladle in Baosteel. UNITECR 1999, Berlin, Germany, 267–268 [5] Zhang, H.; et al.: Study on ladle purging plug with gradient composite structure and material. UNITECR 2013, Victoria, Canada, 621–624 [6] Long, B.; Buhr, A.; Xu, G.Y.: Thermodynamic evaluation and properties of refractory materials for steel ladle purging plugs in the system Al2O3–MgO–CaO. Ceram. Int. 42 (2016) 11930–11940 [7] Long, B.; et al.: Fracture behaviour and microstructure of refractory materials for steel ladle purging plugs in the system Al2O3–MgO–CaO. Ceram. Int. 43 (2017) 9679–9685 [8] Tschegg, E.K.: Testing device and appropriate specimen shapes for tests to measure fracture values (in German). Austrian Patent, AT 390328 B, 1990 [9] National Standard on Refractory (CN), 4th ed., China Refractory National Standard Committee, 2010, 35, 59, 43 [10] Harmuth, H.: Stability of crack propagation associated with fracture energy determined by wedge splitting specimen. Theor. Appl. Fract. Mec. 23 (1995) 103–108 [11] Jin, S.; Gruber, D.; Harmuth, H.: Determination of Young’s modulus, fracture energy and tensile strength of refractories by inverse estimation of a wedge splitting procedure. Engin. Fract. Mech. 116 (2014) 228–236 [12] Hasselman, H.: Thermal stress resistance parameters for brittle refractory ceramics: a compendium. Ceram Bull. 12 (1970) 1033–1037 [13] Harmuth, H.; Bradt, R.C.: Investigation of refractory brittleness by fracture mechanical and fractographic methods. Interceram (2010) 6–10 [14] National Standard on Refractory (CN), 4th ed., China Refractory National Standard Committee, 2010, 315 [15] Slag Atlas. 2nd ed., Düsseldorf 1995, 104 [16] De Aza, A.H.; Pena, P.; De Aza, A.S.: Ternary system Al2O3–MgO–CaO: Part 1, primary phase field of crystallization of spinel in the subsystem MgAl2O4–CaAl4O7–CaO–MgO. J. of Amer. Ceram. Soc. 82 (1999) 2193–2203 [17] De Aza, A.H.; et al.: Ternary system Al2O3–MgO–CaO: part 2. Phase relationships in the subsystem Al2O3–MgAl2O4–CaAl4O7. J. of Amer. Ceram. Soc. 83 (2000) 919–927 [18] Göbbels, M.; Woermann, E.; Jung, J.: The Alrich part of the system CaO–Al2O3–MgO, Part I: Phase relationships. J. of Solid State Chemistry 120 (1995) 358–363 [19] Iyi, N.; Göbbels, M.; Matsui, Y.: The Al-rich part of the system CaO–Al2O3–MgO, Part II: Structure refinement of two new magnetoplumbitrelated phases. J. of Solid State Chemistry 120 (1995) 364–371 [20] Lide, D.R.: Handbook of Chemistry and Physics, 73rd ed. (1992–1993), Boca Raton, FL, 5–18 [21] Sakai, M.; Bradt, R.C.: Fracture toughness testing of brittle materials. Int. Mater. Rev 38 (1993) [2] 53–78